Optical characteristics of LiZnVO4 green phosphor at low temperature preparation
Hsiao, Yu-Jen, Chai, Yin-Lai, Ji, Liang-Wen, Fang, Te-Hua, Meen, Teen-Hang, Tsai, Jenn-Kai, Chen, Kan-Lin and Prior, Stephen D. (2012) Optical characteristics of LiZnVO4 green phosphor at low temperature preparation. Materials Letters, 70 . pp. 163-166. ISSN 0167-577X
- Published Version
Restricted to Middlesex University staff only
Official URL: http://dx.doi.org/10.1016/j.matlet.2011.11.076
This item is available in the Library Catalogue
Photoluminescence characterization of LiZnVO4 oxides by the vibrating milled solid-state reaction was investigated in this work. The products were characterized by X-ray diffraction, scanning electron microscopy, photoluminescence spectroscopy and absorption spectra. The excitation wavelengths associated with charge transfer bands of [VO4]3− are located at 355 nm. The photoluminescence results reveal that the sample prepared at 500 °C exhibits a broad and strong bluish green emission peaks at about 526 nm compared with other samples. Furthermore, the visible light absorption edge of the LiZnVO4 annealed at 500 °C was located at 413 nm, which corresponded to band-gap energy of 3.0 eV.
LiZnVO4 microcrystals were successful prepared by a vibrating milled solid-state reaction. ► Pure rhombohedral LiZnVO4 crystals can be obtained by heat treatment at above 500°C. ► The visible light absorption edge of the sample prepared at 500°C was found to be at 413 nm, which corresponded to a band-gap energy of 3.0 eV.
|Keywords (uncontrolled):||Luminescence; LiZnVO4 oxides; Optical materials and properties|
|Research Areas:||Science & Technology > Science & Technology|
|Citations on ISI Web of Science:||0|
|Permissions granted by publisher:||Copyright © 2011 Elsevier B.V. All rights reserved. Author can archive pre-print and post-print.|
|Deposited On:||11 Jan 2012 05:17|
|Last Modified:||03 Oct 2013 07:00|
Repository Staff Only: item control page
Downloads per month over past year